Karbon low martensitic stainless steel 1.4418, X4CRNIMO16-5-1, Z8CND17.04, S165M, luyu jeung EN 10088-1, hawa 9160. 1.4418 Komposisi kimiawi: Karbon C: ≤0.06 Silicon Si: ≤1.0.06 Silicon Si: ≤ Mangan Mn: 50. P : ≤0.04 Walirang S: ≤0.030 Chromium Cr: 15.00~17.00 Molybdenum Mo: 0.80-1.50 Nikel Ni: 4.00-6.00 Nitrogen N: ≥0.02 1.4418, X4-1.50 Nikel Nikel: ≥0.02 1.4418, X4-1.5Cr-Nitrogen N: ≥0.02 1.4418, X4-6Cr-NiMo -1 langkung saé Salah sahiji sasmita martensit kalayan résistansi korosi anu nyukupan, sipat kakuatan anu saé sareng karasa luhur kalayan eusi karbon anu ngirangan.baja ngabogaan kakuatan pohara alus sarta lalawanan korosi tina mendi dilas, résistansi kacapean, parameter pohara alus dina lingkungan suhu low, sarta lalawanan korosi comparable baja austenitic 18-8.Sajaba ti éta, boga solderability alus.Bahan disadiakeun utamana dina bentuk rod dipaké dina produksi valves, turbin sub-majelis, kacang na bolts, shafts, pin, pistons, shafts utama, crankshafts, agitators dina kimia, tanaga, laut, shipbuilding, aerospace / industri cryogenic.Sipat Mékanis Kakuatan Ngahasilkeun RP0.2 MPA Kakuatan Tensile RM MPA Elongation [%] Teuas [HB] Bar ≥750 900 – 1100 ≥16 280 – 340 QT900 920 1050 18 300

Rujukan prosés perlakuan panas: Austenitizing na quenching dina 950 nepi ka 1050 °C, sarta geuwat tempering dina 600 °C salila 8 jam, lajeng cooling dina hawa.Kumaha weldability?Alus, low-karbon martensit jeung finely dispersed dipikagaduh austenite ngahasilkeun kateguhan HAZ alus teuing dina kaayaan las.Preheating ka 100 ° C - 200 ° C diperlukeun pikeun bagian pisan kandel atawa pikeun konsentrasi stress sanggeus cooling.